Speċifikazzjonijiet Tekniċi
Kompożizzjoni kimika (EN 10025-2)
| Element | Perċentwali (%) |
|---|---|
| Karbonju (Ċ) | Inqas minn jew daqs 0.22 |
| Manganiż (MN) | Inqas minn jew daqs 1.50 |
| Fosfru (P) | Inqas minn jew daqs 0.035 |
| Kubrit (i) | Inqas minn jew daqs 0.035 |
| Silikon (SI) | Inqas minn jew daqs 0.55 |
Propjetajiet mekkaniċi
| Proprjetà | Valur |
|---|---|
| Saħħa tar-rendiment | 275 MPa (min) |
| Qawwa tat-tensjoni | 410–560 MPa |
| Titwil | 20–23% (f'50mm) |
| Enerġija tal-impatt | 27 J fi +20 grad |
| Saħħa tar-rendiment (akbar minn jew daqs n / mm2) | Qawwa tat-tensjoni | |||||||
| Pajjiż | Grad tal-azzar | d inqas minn jew daqs 16 | 16 | 40 | 60 | 100 | 150 | N / mm2 |
|
| Iċ-Ċina | Q235 | 235 | 225 | 215 | 215 | 195 | 185 | 370-500 |
| Us | A36 | 250 MPa (D inqas minn jew daqs 200mm) | 400-550 | |||||
| Ewropew | S235 | 235 | 225 | 215 | 215 | 195 | 185 | 360-510 |
| Ġappun | SS400 | 245 | 235 | 215 | 215 | 205 | 205 | 400-510 |
Pjanċa tal-azzar S275JR, minħabba s-saħħa għolja moderata tagħha, l-ebusija, ir-reżistenza għall-għeja, ir-reżistenza għall-impatt, ir-reżistenza għall-korrużjoni, l-iwweldabilità, u l-faċilità tal-ipproċessar tal-proprjetajiet ta 'kwalità għolja komprensiva - irċeviet b'mod konsistenti tifħir mifrux u rikonoxximent mill-industrija tal-manifattura għall-prestazzjoni tagħha fl-applikazzjoni. Sussegwentement, minħabba r-rikonoxximent tas-soċjetà u l-użu estensiv tagħha fil-manifattura, flimkien ma 'ottimizzazzjoni kontinwa u aġġornament tal-materjal mill-produtturi, il-pjanċa tal-azzar S275JR saret gradwalment waħda mill-gradi tal-azzar użati b'mod komuni fiċ-Ċina.